Abstract Blends of zein and poly(vinyl alcohol) (PVAl) were processed in an internal mixer (150ºC, 50 rpm) for 5-8 minutes. Glycerol and oleic acid were used as plasticizers. The mixtures obtained were then compression molded and further characterized by Fourier transform infrared spectroscopy (FTIR), water-absorption experiments, mechanical tests, and scanning electron microscopy (SEM). FTIR analysis indicated the existence of hydrogen bonding interactions between zein and PVAl. Tensile tests showed that the addition of PVAl increased the flexibility of the blends. The tensile strength ranged from 1.7 to 5.7 MPa, elongation at break ranged from 2.7 to 32% and Young’s modulus ranged from 433 to 7371 MPa. Water absorption at equilibrium decreased with increasing zein content, which favored a brittle behavior in the zein/PVAl. The blends were immiscible in the composition studied and the presence of voids indicated poor interfacial interaction between the polymers.

Abstract Modification of composite components has been proposed as a tool to improve their functional properties. The present work studied crosslinking of a starch/oat hull mixture by reactive extrusion with sodium trimetaphosphate (STMP), for application in composites with polylactic acid (PLA). The treated mixture was characterized regarding degree of substitution, FT-IR, and thermal properties. The native and modified mixtures were processed by injection molding, together with PLA and glycerol. The microstructure, mechanical properties, shrinkage, density, and thermal properties of the composites were determined. The FT-IR results, increase in phosphorus content and thermal stability after starch/fiber mixture treatment with STMP suggested the occurrence of crosslinking. Better interfacial adhesion between oat hulls and the polymeric matrix was observed in electron micrographs of the composites containing the modified components. Slight decreases in tensile strength and modulus were observed in the modified composites, suggesting that extrusion and subsequent milling may have broken some structures/linkages.

Abstract This study investigated the effects of low concentrations of sericin (≤ 1.5 wt%) in starch- poly(butylene-adipate-co-terephthalate) (PBAT) films. The films were produced by blown extrusion and mechanical, barrier and structural properties were determined. Films containing 1.0 and 1.5 wt% sericin showed higher tensile strength (6.41 and 6.59 MPa) and Young's modulus (90.88 and 132.71 MPa) compared with film without sericin (4.76 MPa and 18.64 MPa). When 0.5 wt% of sericin was used, the elongation was reduced by 62%. The addition of sericin in a concentration of 1.5% (w/w) decreased the water vapor permeability of films from 7.55 to 5.94 g (m s Pa)-1, likely due to the formation of a more homogeneous and compact matrix. Based on these results, a mechanism of action is proposed, whereby sericin acts at the interface of the polymers (starch and PBAT), reducing the interfacial tension and enhancing compatibility.

Abstract The aim of this work was to study the relationship of chain size of partially hydrolyzed PVA blended with starch in properties of biodegradable sheets produced by thermoplastic extrusion. It was also studied the effect of extrusion temperature profile to determine the better PVA chain size and temperature profile to produce biodegradable sheets through a factorial design. The processability and the mechanical, thermal, optical, and microstructural properties of the biodegradable sheets were adequate, indicating that PVA/cassava starch blends have potential to replace conventional non-biodegradable polymers. Tensile strength and Young’s modulus ranges from 1.0 to 2.6 and 3.0 to 6.9 MPa respectively, the elongation at break ranges from 42 to 421%. It was not possible to state a conclusive relationship between PVA molecular weight and the materials properties, but in general, PVA with medium molecular weight and high extrusion temperature profile promote an increase of mechanical properties of the sheets.

The extraction of kahweol and cafestol involves saponification reaction. This step is important for the efficiency of the extraction as the diterpenes are susceptible to structural changes during hydrolysis. The microwave-assisted saponification has been successfully used in different matrices, but there is no previous report of the use of this technique in the saponification of diterpenes. Therefore, the effect of microwave-assisted saponification on the extraction of kahweol and cafestol in roasted coffee was evaluated. A 32 factorial experimental design was used in order to evaluate the effect of temperature (70, 80, and 90 ºC) and reaction time (4, 8, and 12 min). The quantification of diterpenes was performed by high-performance liquid chromatography and the results were compared to with those obtained by a method, which uses thermostatic bath for saponification. Temperature and time had a significant effect (p < 0.05) on diterpenes levels. For simultaneous saponification of kahweol and cafestol, the optimal reaction conditions were 80 ºC / 12 min. The use of microwave-assisted procedure lead to lower yields of kahweol (24%) and cafestol (35%) compared to reference method. However a significant reduction of reaction time (80%) was achieved, and the procedure also has the advantage of controlled process conditions and the possibility of extended scale.

Abstract Films and sheets composed by poly (lactic acid) (PLA)/thermoplastic starch (TPS) and TPS/gelatin blends have already been produced and characterized in the literature. However, materials produced with these three biopolymers have not been clearly investigated. In this work, extruded sheets were produced with PLA, TPS (glycerol as plasticizer) and different amounts of gelatin (0, 1, 3 and 5 wt%) in a pilot scale co-rotating twin-screw extruder coupled with a calender. The extruded sheets were characterized in regards to their water solubility, thickness, density, water vapor permeability (WVP), moisture sorption isotherms, mechanical properties and microstructure. The results showed an increase in solubility and WVP besides a decrease of about 30% in tensile strength, Young's modulus and elongation at break. Extruded sheets microstructure revealed smother surfaces and homogeneous morphology with the addition of gelatin. The experiments demonstrated that extrusion and calendering process is a viable way to produce PLA/TPS/gelatin sheets with interesting properties.

Abstract The modification of lignocellulosic fibers can enhance their interaction with other materials and alkaline hydrogen peroxide (AHP) is a reagent widely used to promote such modification. This work aimed to modify oat hulls fibers by reactive extrusion using AHP (7 g 100 g-1 of hulls). The modified oat hulls displayed performances comparable to those observed by other researchers using conventional AHP method (without extrusion). The AHP treated oat hulls showed increased luminosity compared to the extruded ones. Fourier transform infrared spectroscopy showed differences between the modified and unmodified structures. The removal of surface compounds resulted in a more open morphology, with greater surface area and greater porosity. Reactive extrusion can be an alternative method for fiber modification with several advantages, such as short processing time and no wastewater generation.

Abstract The aim of the work was to study the mechanical properties of extruded starch/polyvinyl alcohol (PVA)/glycerol biodegradable blends using multivariate analysis. The blends were produced as cylindrical strands by extrusion using PVAs with different hydrolysis degrees and viscosities, at two extrusion temperature profiles (90/170/170/170/170 °C and 90/170/200/200/200 °C) and three conditioning relative humidities of the samples (33, 53, and 75%). The mechanical properties showed a great variability according to PVA type, as well as the extrusion temperature profile and the conditioning relative humidity; the tensile strength ranged from 0.42 to 5.40 MPa, elongation at break ranged from 10 to 404% and Young’s modulus ranged from 0.93 to 13.81 MPa. The multivariate analysis was a useful methodology to study the mechanical properties behavior of starch/PVA/glycerol blends, and it can be used as an exploratory technique to select of the more suitable PVA type and extrusion temperature to produce biodegradable materials.

Abstract Blends of poly(lactic acid) (PLA) and thermoplastic starch (TPS) plasticized with adipate esters (diisodecyl adipate and diethyl adipate) having different molecular weight were used to produce sheets. The calendering-extrusion process at a pilot scale was used, and the mechanical, barrier, and morphological characterization of the obtained materials were performed. The increase in the TPS content affected the mechanical properties of the sheets by increasing the elongation and decreasing the rigidity. TPS conferred a more hydrophilic character to the sheets, as observed from the water vapor permeability results. The sheets plasticized with diisodecyl adipate (DIA), having a higher molecular weight, had better mechanical and barrier properties than diethyl adipate (DEA) plasticized sheets, indicating that DIA was more effective as plasticizer. Micrographs obtained by confocal laser microscopy and scanning electron microscopy showed different morphologies when different proportions of PLA and TPS were used (dispersed or co-continuous structures), which were strongly associated with the mechanical and barrier properties.

AbstractThe demand for renewably sourced biodegradable materials has increased the need to produce materials that combine appropriate functional properties at competitive costs. Thermoplastic starch and polyester blends are an interesting alternative to current materials due to the low cost of starch and the functional properties and processability of the resulting blends. Producing thermoplastic starch (TPS) requires using a plasticiser at concentrations between 20 and 30%wt (in relation to starch). Glycerol is the most common plasticiser due to its high plasticising capacity and thermal stability at processing temperatures. The objective of this study was to evaluate glycerol waste from the biodiesel industry, with different degrees of purification, as plasticisers for TPS / poly (butylene adipate-co-terephthalate) (PBAT) blends. Different purities of glycerol produced films with similar mechanical, optical and barrier properties to those made with purified glycerol (99.7%). Therefore, crude glycerol is a renewable alternative plasticiser that reduces the cost of plasticisation by 6-fold.

<title>Resumo</title><p>Foram produzidos 12 laminados com diferentes proporções de amido de mandioca, poli(vinil álcool) (PVA) e glicerol por extrusão usando um planejamento de mistura. A opacidade dos materiais variou entre 31 e 56%, e a concentração de PVA e a interação entre as concentrações de amido e PVA foram os principais responsáveis pelo aumento da opacidade. A diferença de cor (ΔE*) variou entre 20-30, sendo a concentração de amido o principal responsável pelo aumento da diferença de cor, por promover uma coloração mais amarelada nos laminados.</p>

<title>Abstract</title><p>Twelve sheets were produced by extrusion with different proportions of cassava starch, poly (vinyl alcohol) (PVA) and glycerol using a mixture design. The opacity of the materials ranged from 31 to 56%, and the concentration of PVA and the interaction between starch and PVA concentrations the mainly responsible for increasing opacity. The color difference (ΔE*) ranged from 20 to 30, the concentration of starch being primarily responsible for increasing in color difference by promoting a more yellowish color in sheets.</p>

AbstractPhytopharmaceutical products are being used in the treatment and prevention of health problems. Nowadays, the development and evaluation of novel pharmaceutical products is expensive and time consuming. A statistical approach is a good tool for optimal development processes. Nectandra falcifolia (Nees) J.A. Castigl. ex Mart. Crov. & Piccinini, Lauraceae, a Brazilian species, is reported as anti-inflammatory, anti-leishmanial and anti-microbial. However, there is little known about its chemical composition. For other species of Nectandra genus, the presence of antioxidant compounds is reported. In order to optimize the process of obtaining extract with high antioxidant activity, different extraction conditions were tested following a statistical approach. Two sequential experimental designs were used – first, a factorial 23 design, followed by central composite 22. The extracts manufactured by these experimental statistical matrixes had their antioxidant activity and phenolic contents quantified and the response surface plots were fitted in quadratic models and they predicted the best extraction condition for the best antioxidant activity. This standardized extract and its antioxidant activity were better evaluated by two complementary tests (ABTS and Burst respiratory). A topical formulation containing 1% (w/w) of standardized extract was prepared and used for an in vivo skin permeation study using a two-dose application. The photoacoustic spectroscopy was used to analyze the samples from the permeation study and the composition profile of standardized extract. In rat skin samples, the data demonstrated that for the higher dose of topical formulation (5 g/cm2), the standardized extract could cross skin and be seen in epidermis and dermis. This was not the case for the lower dose (2 g/cm2) which was only present in the epidermis. This information suggests that this novel standardized extract of N. falcifoliacould be explored for skin damage prevention or treatment for diseases developed by oxidative damage.

O objetivo do trabalho foi determinar a duração do ciclo de produção e a necessidade térmica de seis clones de 'Concord' sobre três porta-enxertos no norte do Paraná. Foram avaliados os clones '22', '28', '49', '202', '211' e '225', obtidos pela Embrapa Uva e Vinho, e enxertados sobre os porta-enxertos 'IAC 766', 'IAC 572' e '420-A'. O trabalho foi realizado em área experimental pertencente ao Centro Tecnológico da COROL - Cooperativa Agroindustrial, localizado no município de Rolândia-PR. O experimento foi realizado em esquema fatorial (6 clones x 3 porta-enxertos), em delineamento inteiramente casualizado, com cinco repetições. As plantas foram conduzidas em sistema de latada, no espaçamento de 4,0 m x 2,0 m, e as avaliações foram realizadas nas safras de 2009/2010 e 2010/2011. Verificou-se que dentre os clones de 'Concord' avaliados, o '202' apresenta a menor duração do ciclo entre a poda e a colheita, sendo portanto o mais precoce. Dentre os porta-enxertos, o '420-A' induz a maior taxa de acúmulo diário de sólidos solúveis do mosto, proporcionando redução do ciclo total e da demanda térmica dos clones de 'Concord', enquanto o 'IAC 572' induz a menor taxa, promovendo aumento do ciclo e da demanda térmica dos clones.

The aim of this study was to determine the duration of the production cycle and the thermal requirement of six clones of the 'Concord' grapevine, on three rootstocks, in the North of Paraná. The 'Concord' clones '22', '28', '49', '202', '211' and '225', obtained by Embrapa Grape and Wine, were evaluated grafted on '420-A', 'IAC 766' and 'IAC 572' rootstocks. The trial was carried out in an experimental vineyard located at the Technology Center of COROL Cooperative, in Rolândia, PR. A completely randomized design was used as statistical model, arranged in a factorial system (six clones x three rootstocks) with five replications. The grapevines were trained in a overhead trellis system, spaced at 4.0 x 2.0 m. The evaluations were performed during the harvest of 2009/2010 and 2010/2011. It was verified that '202' is the earliest 'Concord' clone, by showing the lowest cycle duration from pruning to harvest. Among the rootstocks, the '420-A' induces the highest daily rate accumulation of solid soluble, reducing the total cycle and the thermal demand, while the 'IAC 572' induces the lowest rate, increasing the cycle and the thermal demand of the clones.

The production of plant seedlings has traditionally used polyethylene bags, which are thrown out in the soil or burned after transplant because the large amount of organic material attached to the bags makes recycling difficult. Additionally, when a seedling is taken from the bag for transplant, there is the risk of root damage, which compromises the plant’s development. In this study, we developed biodegradable bags to be used in seedling production, and we verify their influence on the development of Brazilian ginseng (Pfaffia glomerata (Spreng) Pedersen), when the plant is planted without being removed from the bag. Both black and white biodegradable bags remained intact throughout the seedling production period (60 days). After being transplanted into containers (240 days), they were completely biodegraded, and there was no significant difference between the dry mass of these plants and that of plants that were transplanted without the bags. The plants that were cultivated without being removed from the polyethylene bags had root development difficulties, and the wrapping showed no signs of degradation. The use of biodegradable films is an alternative for the production of bags for seedlings, as these can then be transplanted directly into the soil without removing the bag, reducing the risk of damage to the roots during the moment of transplant.

This study aims to prepare biodegradable films from cassava starch, poly (butylene adipate-co-terephthalate) (PBAT), and montmorillonite (MMT) using blow-extrusion process and analyze the effects of different types and concentrations of MMT on the microstructure, physicochemical, and mechanical properties of the resulting films. The films were produced by blending 30% of PBAT with glycerol (17.5%), starch (49.0-52.5%), and four different types of montmorillonite (Cloisite® Na+, 10A, 15A, and 30B) at two different concentrations (1.75% and 3.5%). All the films prepared in this study showed an increase in the basal spacing of MMT layers. In particular, the films with 10A and 30B showed the highest increase in intercalation basal spacing, suggesting the formation of intercalated composites. The addition of nanoclays decreased the elongation of films. The addition of Cloisite® 10A resulted in films with the lowest WVP values and the highest stability to water adsorption under different RH conditions.